sillica
| Parameter | Unit | Results | Method |
|---|---|---|---|
| Iron Trioxide (Fe₂O₃) | % | 0.02 | PO / MIN-BT / 01 |
| Aluminium Trioxide (Al₂O₃) | % | 0.01 | PO / MIN-BT / 01 |
| Calcium Oxide (CaO) | % | 0.01 | PO / MIN-BT / 01 |
| Magnesium Oxide (MgO) | % | Less than 0.01 | PO / MIN-BT / 01 |
| Manganese Dioxide (MnO₂) | % | 0.02 | PO / MIN-BT / 01 |
| Chromium Trioxide (Cr₂O₃) | % | Less than 0.01 | PO / MIN-BT / 01 |
| Sodium Oxide (Na₂O) | % | Less than 0.01 | PO / MIN-BT / 01 |
| Potassium Oxide (K₂O) | % | Less than 0.01 | PO / MIN-BT / 01 |
| Silicon Dioxide (SiO₂) | % | 99.42 | PO / MIN-BT / 01 |
| Titanium Dioxide (TiO₂) | % | 0.03 | PO / MIN-BT / 01 |
| Loss On Ignition (LOI) | % | 0.06 | PO / MIN-BT / 01 |
| Moisture Content (MC) | %, AR | 4.55 | PO / MIN-BT / 01 |